edoc-Server der Humboldt-Universität zu Berlin

Dissertation

Autor(en): Dillip Kumar Satapathy
Titel: Molecular-beam epitaxy growth and structural characterization of semiconductor-ferromagnet heterostructures by grazing incidence x-ray diffraction
Gutachter: A. D. Wieck; Klaus H. Ploog; W. T. Masselink
Erscheinungsdatum: 05.12.2006
Volltext: pdf (urn:nbn:de:kobv:11-10073003)
Fachgebiet(e): Physik
Schlagwörter (ger): Molekularstrahlepitaxie, Ferromagnet-Halbleiter Hybridstrukturen, Dünne Schichten, Beugung unter streifendem Einfall, Beugung hochenergetischer Elektronen, Periodische Versetzungsnetzwerke, Grenzfläche
Schlagwörter (eng): Ferromagnet-semiconductor hybrid structures, Molecular beam epitaxy, Thin films, Grazing incidence diffraction, Relfection high-energy electron diffraction, Periodic dislocation array, Interface
Einrichtung: Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I
Zitationshinweis: Satapathy, Dillip Kumar: Molecular-beam epitaxy growth and structural characterization of semiconductor-ferromagnet heterostructures by grazing incidence x-ray diffraction; Dissertation, Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I , publiziert am 05.12.2006, urn:nbn:de:kobv:11-10073003
Metadatenexport: Um den gesamten Metadatensatz im Endnote- oder Bibtex-Format zu speichern, klicken Sie bitte auf den entsprechenden Link. Endnote   Bibtex  
print on demand: Wenn Sie auf dieses Icon klicken, können Sie ein Druckexemplar dieser Publikation bestellen.
Diese Seite taggen: Diese Icons führen auf so genannte Social-Bookmark-Systeme, auf denen Sie Lesezeichen anlegen, persönliche Tags vergeben und Lesezeichen anderer Nutzer ansehen können.
  • connotea
  • del.icio.us
  • Furl
  • RawSugar

Abstract (ger):
Diese Arbeit behandelt das Wachstum des ferromagnetischen Metalls MnAs auf halbleitendem GaAs. Die MnAs-Filme werden auf GaAs mittels der Molekularstrahlepitaxie (MBE) abgeschieden. Nukleation, Entwicklung von Gitterverzerrungen, Morphologie und Grenzflächenstruktur werden in-situ während des MBE Wachstums mit Hilfe von Beugung unter streifendem Einfall (GID) und der Beugung hochenergetischer Elektronen (RHEED) untersucht. Mit azimuthalen RHEED Messungen wurden vier Abschnitte des Nukleationsprozesses von MnAs auf GaAs(001) bestimmt. GID Messungen zeigen, dass das weitere Wachstum des MnAs Films bei einer nominellen Bedeckung von 2.5 ML über die Bildung relaxierter Inseln erfolgt, welche an Größe zunehmen und schließlich einen durchgängigen Film bilden. In einem Frühstadium bildet sich ein geordnetes Versetzungsnetzwerk an der Grenzfläche, welches die Verzerrungen aufgrund der Fehlanpassung bereits vor der vollständigen Ausbildung des durchgängigen Films abbauen. Der faszinierend komplexe Nukleationsprozess von MnAs auf GaAs(0 0 1) beinhaltet sowohl Elemente von Volmer-Weber, als auch von Stranski-Krastanov Wachstum. Die nicht einheitliche Gitterfehlanpassung beträgt 0.66% entlang der [1 -1 0] Richtung und 0.54% entlang der [1 1 0] Richtung, wie sich aus den Röntgenbeugungsmessungen ergibt. Entlang der [1 1 0] Richtung wird eine hohe Korrelation der Defekte beobachtet. Ein hochgradig periodisches Versetzungsnetzwerk mit einer Periode von 4.95 +- 0.05 nm entlang der [1 1 0] Richtung wird an der Grenzfläche gebildet und relaxiert 7.5% der Fehlanpassung. Die inhomogenen Verzerrungen aufgrund dieser periodischen Versetzungen an der Grenzfläche sind auf eine Schicht von 1.6nm Dicke beschränkt. Die Fehlanpassung entlang der [1 -1 0] Richtung wird durch die Bildung eines Koinzidenzgitters abgebaut.
Abstract (eng):
The present work is devoted to the growth of the ferromagnetic metal MnAs on the semiconductor GaAs by molecular-beam epitaxy (MBE). The MnAs thin films are deposited on GaAs by molecular-beam epitaxy (MBE). Grazing incidence diffraction (GID) and reflection high-energy electron diffraction (RHEED) are used in situ to investigate the nucleation, evolution of strain, morphology and interfacial structure during the MBE growth. Four stages of the nucleation process during growth of MnAs on GaAs(001) are revealed by RHEED azimuthal scans. GID shows that further growth of MnAs films proceed via the formation of relaxed islands at a nominal thickness of 2.5 ML which increase in size and finally coalesce to form a continuous film. Early on, an ordered array of misfit dislocations forms at the interface releasing the misfit strain even before complete coalescence occurs. The fascinatingly complex nucleation process of MnAs on GaAs(0 0 1) contains elements of both Volmer-Weber and Stranski-Krastanov growth. A nonuniform strain amounting to 0.66%, along the [1 -1 0] direction and 0.54%, along the [1 1 0] direction is demonstrated from x-ray line profile analysis. A high correlation between the defects is found along the GaAs[1 1 0] direction. An extremely periodic array of misfit dislocations with a period of 4.95 +- 0.05 nm is formed at the interface along the [1 1 0] direction which releases the 7.5% of misfit. The inhomogeneous strain due to the periodic dislocations is confined at the interface within a layer of 1.6 nm thickness. The misfit along the [1 -1 0] direction is released by the formation of a coincidence site lattice.
Zugriffsstatistik: Die Daten für die Zugriffsstatistik der einzelnen Dokumente wurden aus den durch AWStats aggregierten Webserver-Logs erstellt. Sie beziehen sich auf den monatlichen Zugriff auf den Volltext sowie auf die Startseite. Die Zugriffsstatistik wird nicht standardisiert erfasst und kann maschinelle Zugriffe enthalten.
 
Bei Formatversionen eines Dokuments, die aus mehreren Dateien bestehen (insbesondere HTML), wird jeweils der monatlich höchste Zugriffswert auf eine der Dateien (Kapitel) des Dokuments angezeigt.
 
Um die detaillierten Zugriffszahlen zu sehen, fahren Sie bitte mit dem Mauszeiger über die einzelnen Balken des Diagramms.
Startseite: 2 Zugriffe PDF: 3 Zugriffe Startseite: 3 Zugriffe PDF: 5 Zugriffe Startseite: 3 Zugriffe PDF: 4 Zugriffe PDF: 3 Zugriffe Startseite: 3 Zugriffe PDF: 8 Zugriffe Startseite: 1 Zugriffe PDF: 3 Zugriffe PDF: 9 Zugriffe PDF: 7 Zugriffe PDF: 5 Zugriffe Startseite: 1 Zugriffe PDF: 8 Zugriffe Startseite: 3 Zugriffe PDF: 11 Zugriffe PDF: 13 Zugriffe PDF: 9 Zugriffe PDF: 9 Zugriffe PDF: 13 Zugriffe PDF: 13 Zugriffe PDF: 17 Zugriffe PDF: 15 Zugriffe Startseite: 2 Zugriffe PDF: 15 Zugriffe Startseite: 1 Zugriffe PDF: 22 Zugriffe PDF: 31 Zugriffe Startseite: 1 Zugriffe PDF: 28 Zugriffe PDF: 18 Zugriffe PDF: 14 Zugriffe Startseite: 3 Zugriffe PDF: 23 Zugriffe Startseite: 3 Zugriffe PDF: 20 Zugriffe Startseite: 1 Zugriffe PDF: 27 Zugriffe Startseite: 4 Zugriffe PDF: 22 Zugriffe Startseite: 2 Zugriffe PDF: 23 Zugriffe PDF: 37 Zugriffe Startseite: 1 Zugriffe PDF: 52 Zugriffe
Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
Apr
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Monat Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
Apr
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Startseite 2 3 3   3 1       1 3               2 1   1     3 3 1 4 2   1
PDF 3 5 4 3 8 3 9 7 5 8 11 13 9 9 13 13 17 15 15 22 31 28 18 14 23 20 27 22 23 37 52

Gesamtzahl der Zugriffe seit Jul 2011:

  • Startseite – 34 (1.1 pro Monat)
  • PDF – 487 (15.71 pro Monat)
 
 
Generiert am 24.04.2014, 02:46:46