Dissertation

Autor(en): Ulf Seidel
Titel: Grenzflächenuntersuchungen am Tunnelkontakt einer MOCVD-präparierten Tandemsolarzelle
Gutachter: R. Manzke; T. Hannappel; M. Heuken
Erscheinungsdatum: 04.09.2007
Volltext: pdf (urn:nbn:de:kobv:11-10081159)
Fachgebiet(e): Physik
Schlagwörter (ger): Grenzfläche, Solarzellen, III-V-Halbleiter, Oberflächenrekonstruktion, Tunneldiode
Schlagwörter (eng): interface, III-V semiconductors, solar cells, surface reconstruction, tunnel diode
Einrichtung: Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I
Zitationshinweis: Seidel, Ulf: Grenzflächenuntersuchungen am Tunnelkontakt einer MOCVD-präparierten Tandemsolarzelle; Dissertation, Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I , publiziert am 04.09.2007, urn:nbn:de:kobv:11-10081159
Metadatenexport: Um den gesamten Metadatensatz im Endnote- oder Bibtex-Format zu speichern, klicken Sie bitte auf den entsprechenden Link. Endnote   Bibtex  
print on demand: Wenn Sie auf dieses Icon klicken, können Sie ein Druckexemplar dieser Publikation bestellen.
Diese Seite taggen: Diese Icons führen auf so genannte Social-Bookmark-Systeme, auf denen Sie Lesezeichen anlegen, persönliche Tags vergeben und Lesezeichen anderer Nutzer ansehen können.
  • connotea
  • del.icio.us
  • Furl
  • RawSugar

Abstract (ger):
In dieser Arbeit wurde eine Tandemsolarzelle aus III-V-Halbleitern auf der Gitterkonstanten von InP mit einem neuartigen Tunnelkontakt entwickelt. Für die Entwicklung der monolithischen Präparation wurden insbesondere kritische Hetero-Grenzflächen im Bereich des Tunnelkontaktes mit oberflächensensitiven Messmethoden untersucht. Die Tandemsolarzelle bestand aus Einzelsolarzellen mit Absorberschichten aus InGaAs (E_g=0,73eV) und InGaAsP (E_g=1,03eV), deren Serienverschaltung mit einem Tunnelkontakt erfolgte, der aus einer n-InGaAs- und einer p-GaAsSb-Schicht bestand. Die Halbleiterschichten wurden mit metallorganischer Gasphasenepitaxie (MOCVD) einkristallin auf einem InP(100)-Substrat gitterangepasst präpariert. Insbesondere wurde der Einfluss der Präparation von InGaAs-Oberflächen auf die Schärfe der InGaAs/GaAsSb-Grenzfläche in-situ mit RAS und nach einem kontaminationsfreien Transfer ins UHV mit UPS, XPS und LEED untersucht. Dabei konnten erstmals drei verschiedene Rekonstruktionen der MOCVD-präparierten InGaAs-Oberfläche beobachtet werden, die von der Heiztemperatur abhängig waren: eine As-reiche (4x3)-, eine InGa-reiche (2x4)- und eine ebenfalls InGa-reiche (4x2)/c(8x2)-Rekonstruktion. Danach erfolgte die Untersuchung des Wachstums von dünnen GaAsSb-Schichten auf diesen drei InGaAs-Oberflächen. Anhand des Sb/As-Verhältnisses im GaAsSb konnte die Präparation auf der (4x3)-rekonstruierten Oberfläche als die schlechteste beurteilt werden. Abschließend wurden Tandemsolarzellen mit verschieden dicken Absorberschichten der InGaAsP-Topzelle gefertigt. Der höchste Wirkungsgrad einer hier hergestellten Tandemsolarzelle betrug 7,3% unter einem gefilterten Sonnenspektrum, das eine GaAs-basierte Tandemsolarzelle mit großen Bandlücken (E_g>1,4eV) simulierte. Die Kombination einer solchen Tandemsolarzelle mit der hier entwickelten InGaAs/InGaAsP-Tandemsolarzelle hat das Potential, für konzentriertes Sonnenlicht eine Konversionseffizienz von deutlich über 40% zu erreichen.
Abstract (eng):
A monolithic low band gap tandem solar cell made up of III-V semiconductors lattice matched to InP and including a novel tunnel junction was developed. Critical hetero interfaces were investigated in detail, in particular the ones related to the tunnel diode. The tandem solar cell was composed of single junction cells with InGaAs (E_g=0.73eV) and InGaAsP (E_g=1.03eV) absorber layers. The serial connection of the subcells was realized by using a tunnel junction including n-InGaAs and p-GaAsSb layers. Metal organic vapor phase epitaxy (MOVPE) was used to prepare the III-V layers lattice matched on InP(100) substrates. In particular, the influence of the preparation of the InGaAs surface on the sharpness of the InGaAs/GaAsSb interface was investigated in-situ by Reflection Anisotropy Spectroscopy (RAS). After a contamination free transfer to UHV the samples were analyzed by UPS, XPS and LEED. Three different surface reconstructions of MOVPE-prepared InGaAs were determined for the first time: an As-rich (4x3)-, an InGa-rich (2x4) and an also InGa-rich (4x2)/c(8x2)-reconstructed surface. In a second step, the growth of thin GaAsSb layers on the three different InGaAs surfaces was studied. The Sb/As-ratio in the GaAsSb layer indicated that the preparations on the InGa-rich surfaces result in a sharper interface. Finally, tandem solar cells with different thicknesses for the absorber layer of the top cell were produced. The highest efficiency obtained for the tandem solar cell was 7.3%, when measured under a filtered solar spectrum to simulate the operation below a GaAs-based tandem solar cell (E_g>1.4eV). The combination of a high band gap tandem solar cell with the InGaAs/InGaAsP tandem solar cell developed here is estimated to reach under a concentrated solar spectrum a total efficiency of more than 40% after further optimization steps.
Zugriffsstatistik: Die Daten für die Zugriffsstatistik der einzelnen Dokumente wurden aus den durch AWStats aggregierten Webserver-Logs erstellt. Sie beziehen sich auf den monatlichen Zugriff auf den Volltext sowie auf die Startseite. Die Zugriffsstatistik wird nicht standardisiert erfasst und kann maschinelle Zugriffe enthalten.
 
Bei Formatversionen eines Dokuments, die aus mehreren Dateien bestehen (insbesondere HTML), wird jeweils der monatlich höchste Zugriffswert auf eine der Dateien (Kapitel) des Dokuments angezeigt.
 
Um die detaillierten Zugriffszahlen zu sehen, fahren Sie bitte mit dem Mauszeiger über die einzelnen Balken des Diagramms.
Startseite: 4 Zugriffe PDF: 6 Zugriffe Startseite: 1 Zugriffe PDF: 1 Zugriffe Startseite: 11 Zugriffe PDF: 11 Zugriffe Startseite: 1 Zugriffe PDF: 5 Zugriffe Startseite: 6 Zugriffe PDF: 5 Zugriffe PDF: 1 Zugriffe Startseite: 7 Zugriffe PDF: 9 Zugriffe PDF: 20 Zugriffe PDF: 28 Zugriffe Startseite: 4 Zugriffe PDF: 32 Zugriffe Startseite: 5 Zugriffe PDF: 30 Zugriffe Startseite: 2 Zugriffe PDF: 43 Zugriffe PDF: 24 Zugriffe PDF: 27 Zugriffe PDF: 33 Zugriffe PDF: 23 Zugriffe Startseite: 4 Zugriffe PDF: 32 Zugriffe Startseite: 1 Zugriffe PDF: 32 Zugriffe Startseite: 1 Zugriffe PDF: 46 Zugriffe Startseite: 4 Zugriffe PDF: 51 Zugriffe Startseite: 1 Zugriffe PDF: 44 Zugriffe Startseite: 6 Zugriffe PDF: 62 Zugriffe Startseite: 3 Zugriffe PDF: 41 Zugriffe Startseite: 3 Zugriffe PDF: 38 Zugriffe Startseite: 3 Zugriffe PDF: 40 Zugriffe Startseite: 2 Zugriffe PDF: 43 Zugriffe Startseite: 2 Zugriffe PDF: 50 Zugriffe Startseite: 1 Zugriffe PDF: 62 Zugriffe Startseite: 2 Zugriffe PDF: 46 Zugriffe Startseite: 2 Zugriffe PDF: 57 Zugriffe PDF: 46 Zugriffe Startseite: 3 Zugriffe PDF: 88 Zugriffe Startseite: 5 Zugriffe PDF: 69 Zugriffe Startseite: 1 Zugriffe PDF: 67 Zugriffe
Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Apr
14
May
14
Jun
14
Jul
14
Monat Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Apr
14
May
14
Jun
14
Jul
14
Startseite 4 1 11 1 6   7     4 5 2         4 1 1 4 1 6 3 3 3 2 2 1 2 2   3 5 1
PDF 6 1 11 5 5 1 9 20 28 32 30 43 24 27 33 23 32 32 46 51 44 62 41 38 40 43 50 62 46 57 46 88 69 67

Gesamtzahl der Zugriffe seit Jul 2011:

  • Startseite – 85 (2.5 pro Monat)
  • PDF – 1212 (35.65 pro Monat)
 
 
Generiert am 22.08.2014, 22:52:38