Dissertation

Autor(en): Ingo Salzmann
Titel: Structural and energetic properties of pentacene derivatives and heterostructures
Gutachter: Norbert Koch; Wolfgang Neumann; Roland Resel
Erscheinungsdatum: 09.03.2009
Volltext: pdf (urn:nbn:de:kobv:11-10097621)
Fachgebiet(e): Physik
Schlagwörter (ger): Röntgenbeugung, Photoelektronenspektroskopie, organische Halbleiter, organische Solarzellen
Schlagwörter (eng): photoelectron spectroscopy, organic semiconductors, organic photovoltaic cells, x-ray diffraction
Einrichtung: Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I
Zitationshinweis: Salzmann, Ingo: Structural and energetic properties of pentacene derivatives and heterostructures; Dissertation, Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I , publiziert am 09.03.2009, urn:nbn:de:kobv:11-10097621
Metadatenexport: Um den gesamten Metadatensatz im Endnote- oder Bibtex-Format zu speichern, klicken Sie bitte auf den entsprechenden Link. Endnote   Bibtex  
print on demand: Wenn Sie auf dieses Icon klicken, können Sie ein Druckexemplar dieser Publikation bestellen.
Diese Seite taggen: Diese Icons führen auf so genannte Social-Bookmark-Systeme, auf denen Sie Lesezeichen anlegen, persönliche Tags vergeben und Lesezeichen anderer Nutzer ansehen können.
  • connotea
  • del.icio.us
  • Furl
  • RawSugar

Abstract (ger):
Das Ziel der Arbeit ist die Herstellung und die Charakterisierung von Heterostrukturen des organischen Halbleiters Pentazen (PEN) mit diversen konjugierten organischen Materialien im Hinblick auf das Anwendungspotenzial im Bereich der organischen Elektronik. Für die Untersuchung von PEN-Heterostrukturen mit (i) Fulleren (C60), (ii) Perfluoropentazen (PFP) und (iii) 6,13-Pentazenchinon (PQ) wurden mehrere komplementäre experimentelle Techniken angewendet: Röntgenbeugung, Schwingungsspektroskopie, Rasterkraftmikroskopie und Photoelektronenspektroskopie. (i) Für PEN - Heterostrukturen mit C60 wurden die elektronischen, strukturellen und morphologischen Eigenschaften mit der Leistung von organischen Solarzellen (OSZ) für geschichtete und gemischte Systeme korreliert. Dabei wurde gezeigt, dass morphologische anstatt struktureller oder energetischer Ursachen die Leistungsunterschiede der beiden untersuchten Zelltypen erklären. (ii) Strukturuntersuchungen wurden an reinen PFP-Filmen, sowie an geschichteten und gemischten Heterostrukturen mit PEN durchgeführt. Es wurde die Struktur der PFP-Dünnfilmphase gelöst und das Wachstum von PEN+PFP Mischkristallen gezeigt, welche erfolgreich angewandt wurden, um die Ionisationsenergie (IE) des Films mit dem Mischungsverhältnis durchzustimmen. Dies wurde durch die Existenz von innermolekularen polaren Bindungen (C-H und C-F für PEN und PFP) erklärt. (iii) Für reine PQ-Filme wurde die Struktur der PQ-Dünnfilmphase gelöst (ein Molekül pro Einheitszelle). Es wurde eine stark orientierungsabhängige IE von PQ und PEN gefunden und gezeigt, dass die Energieniveaulagen für die Anwendung in OSZ geeignet sind. Die Untersuchung von Mischsystemen zeigte phasensepariertes Wachstum ohne Hinweise auf Interkalation, selbst bei PQ Konzentrationen von nur 2%. Weiters wurde gezeigt, dass O2 und Wasser keine nachhaltigen Auswirkungen auf PEN-Filme zeigen, wohingegen Singlett-Sauerstoff und Ozon diese angreifen und flüchtige Reaktionsprodukte liefern.
Abstract (eng):
The scope of this work is the combination of the organic semiconductor pentacene (PEN) with different conjugated organic molecules to form application relevant heterostructures in vacuum sublimed films. Using x-ray diffraction (XRD), vibrational spectroscopy, atomic force microscopy and photoelectron spectroscopy, PEN heterostructures with (i) fullerene (C60), (ii) perfluoropentacene (PFP) and (iii) 6,13-pentacenequinone (PQ) were thoroughly characterized to judge on the respective application potential in organic electronics. (i) PEN heterostructures with C60 were investigated regarding the correlation of energetic, structural and morphological properties with the performance of organic photovoltaic cells (OPVCs) for both layered and mixed structures. Morphological rather than energetic or structural issues account for performance differences of bulk-heterojunction OPVCs compared to layered devices. (ii) XRD investigations were carried out on pure PFP films, on layered and mixed heterostructures with PEN. The thin-film polymorph of PFP was solved and it is shown that blended films form a mixed crystal structure, which led to the finding that the ionization energy (IE) of organic films composed of molecules with intramolecular polar bonds (like C-H and C-F for PEN and PFP, respectively) can be tuned through the mixing ratio. (iii) A so far unknown thin-film polymorph of PQ on SiO2 substrates was solved using XRD reciprocal space mapping evidencing a loss of the herringbone arrangement known from the PQ bulk structure. For PEN heterostructures with PQ a highly molecular-orientation dependent IE and energy level offsets interesting for the use in OPVCs were found. Mixed films of PEN and PQ exhibit phase separation and no intercalation was found even at PQ concentrations as low as 2%. Finally, it is shown that O2 and water do not react noticeably with PEN, whereas singlet oxygen and ozone readily oxidize PEN films producing volatile reaction products instead of PQ.
Zugriffsstatistik: Die Daten für die Zugriffsstatistik der einzelnen Dokumente wurden aus den durch AWStats aggregierten Webserver-Logs erstellt. Sie beziehen sich auf den monatlichen Zugriff auf den Volltext sowie auf die Startseite. Die Zugriffsstatistik wird nicht standardisiert erfasst und kann maschinelle Zugriffe enthalten.
 
Bei Formatversionen eines Dokuments, die aus mehreren Dateien bestehen (insbesondere HTML), wird jeweils der monatlich höchste Zugriffswert auf eine der Dateien (Kapitel) des Dokuments angezeigt.
 
Um die detaillierten Zugriffszahlen zu sehen, fahren Sie bitte mit dem Mauszeiger über die einzelnen Balken des Diagramms.
Startseite: 6 Zugriffe PDF: 16 Zugriffe Startseite: 2 Zugriffe PDF: 8 Zugriffe Startseite: 4 Zugriffe PDF: 4 Zugriffe Startseite: 3 Zugriffe PDF: 21 Zugriffe Startseite: 13 Zugriffe PDF: 16 Zugriffe Startseite: 6 Zugriffe PDF: 12 Zugriffe Startseite: 6 Zugriffe PDF: 24 Zugriffe PDF: 24 Zugriffe PDF: 27 Zugriffe Startseite: 2 Zugriffe PDF: 35 Zugriffe Startseite: 4 Zugriffe PDF: 25 Zugriffe Startseite: 1 Zugriffe PDF: 9 Zugriffe PDF: 12 Zugriffe PDF: 22 Zugriffe PDF: 22 Zugriffe PDF: 16 Zugriffe Startseite: 2 Zugriffe PDF: 23 Zugriffe Startseite: 2 Zugriffe PDF: 36 Zugriffe Startseite: 2 Zugriffe PDF: 19 Zugriffe Startseite: 6 Zugriffe PDF: 23 Zugriffe Startseite: 1 Zugriffe PDF: 24 Zugriffe PDF: 17 Zugriffe Startseite: 7 Zugriffe PDF: 35 Zugriffe Startseite: 3 Zugriffe PDF: 25 Zugriffe Startseite: 2 Zugriffe PDF: 16 Zugriffe Startseite: 5 Zugriffe PDF: 41 Zugriffe Startseite: 23 Zugriffe PDF: 21 Zugriffe Startseite: 4 Zugriffe PDF: 23 Zugriffe Startseite: 3 Zugriffe PDF: 38 Zugriffe PDF: 28 Zugriffe Startseite: 2 Zugriffe PDF: 40 Zugriffe Startseite: 6 Zugriffe PDF: 51 Zugriffe PDF: 56 Zugriffe Startseite: 2 Zugriffe PDF: 44 Zugriffe Startseite: 2 Zugriffe PDF: 42 Zugriffe PDF: 28 Zugriffe Startseite: 2 Zugriffe PDF: 40 Zugriffe
Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
Apr
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Apr
14
May
14
Jun
14
Jul
14
Aug
14
Sep
14
Monat Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
Apr
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Apr
14
May
14
Jun
14
Jul
14
Aug
14
Sep
14
Startseite 6 2 4 3 13 6 6     2 4 1         2 2 2 6 1   7 3 2 5 23 4 3   2 6   2 2   2
PDF 16 8 4 21 16 12 24 24 27 35 25 9 12 22 22 16 23 36 19 23 24 17 35 25 16 41 21 23 38 28 40 51 56 44 42 28 40

Gesamtzahl der Zugriffe seit Jul 2011:

  • Startseite – 121 (3.27 pro Monat)
  • PDF – 963 (26.03 pro Monat)
 
 
Generiert am 21.10.2014, 12:26:33