Dissertation

Autor(en): Hannes Krüger
Titel: Niedertemperatur Sol-Gel Verfahren für optische Schichtsysteme auf Basis von Magnesiumfluorid und Titandioxid
Gutachter: Erhard Kemnitz; Uwe Beck; Nicolaus P. Ernsting
Erscheinungsdatum: 25.03.2009
Volltext: pdf (urn:nbn:de:kobv:11-10098741)
Fachgebiet(e): Chemie
Schlagwörter (ger): Sol-Gel, Spin-Coating, Ellipsometrie, optische Eigenschaften, optische Schichtsysteme, MgF2, TiO2
Schlagwörter (eng): optical properties, sol-gel, spin-coating, ellipsometry, optical thin films, MgF2, TiO2
Einrichtung: Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I
Zitationshinweis: Krüger, Hannes: Niedertemperatur Sol-Gel Verfahren für optische Schichtsysteme auf Basis von Magnesiumfluorid und Titandioxid; Dissertation, Humboldt-Universität zu Berlin, Mathematisch-Naturwissenschaftliche Fakultät I , publiziert am 25.03.2009, urn:nbn:de:kobv:11-10098741
Metadatenexport: Um den gesamten Metadatensatz im Endnote- oder Bibtex-Format zu speichern, klicken Sie bitte auf den entsprechenden Link. Endnote   Bibtex  
print on demand: Wenn Sie auf dieses Icon klicken, können Sie ein Druckexemplar dieser Publikation bestellen.

Abstract (ger):
Im Rahmen dieser Arbeit wurde ein Niedertemperatur Sol-Gel Spin-Coating Verfahren entwickelt, mit dem sich Metalloxide und -fluoride in Form von Nanometer-dicken Schichten abscheiden lassen. Ziel dieses Verfahrens ist die Herstellung von anti- (AR) und hoch reflektierenden (HR) Schichtsystemen, die aus einem alternierenden Aufbau von niedrig brechenden und hoch brechenden Materialien bestehen. Zur Darstellung der Metallfluoride wurde dabei eine neuartige nichtwässrige Sol-Gel Synthese ausgehend von Metallalkoxiden und in Alkoholen einkondensiertem Fluorwasserstoff angewendet. Die abgeschiedenen Schichten, die bei 100 °C getrocknet wurden, sind mit REM, TEM und AFM auf ihre morphologische Struktur, mit EDX und XPS auf ihre chemische Zusammensetzung und mit Ellipsometrie und UV-vis Transmissionsspektroskopie auf ihre optischen Eigenschaften hin untersucht worden. Mit diesem Verfahren gelang die Präparation von homogenen MgF2- und TiO2-Schichten mit geringen Rauheiten (Ra < 2,0 nm) auf Si- und SiO2-Substraten. Die MgF2-Schichten haben einen Brechungsindex von n500 = 1,36. Die TiO2-Schichten weisen einen Brechungsindex von n500 = 2,05 auf. Die Dicken der MgF2- und TiO2-Schichten sind zwischen 25 nm und 500 nm einstellbar. Durch einen alternierenden Aufbau von MgF2- und TiO2-Schichten gelang außerdem erstmalig die Herstellung von Metallfluorid- und Metalloxid-basierten Schichtsystemen über einen Niedertemperatur Sol-Gel Prozess. Mit Hilfe der bestimmten optischen Eigenschaften der MgF2- und TiO2-Einzelschichten wurden einfache AR und HR Designs entwickelt und aufgebaut. Die Transmissionsspektren der Designs und der jeweiligen Schichtsysteme zeigten dabei gute Übereinstimmungen, gleiches galt für die mit Hilfe der Spektralellipsometrie aufgenommenen Reflexionsspektren. In dieser Arbeit konnte erstmals gezeigt werden, dass sich das Niedertemperatur Sol-Gel Verfahren prinzipiell zur Herstellung von einfachen AR und HR Schichtsystemen eignet.
Abstract (eng):
This work deals with the development of a low temperature sol-gel spincoating process for thin films with thicknesses in the nanometer range based on metal oxides and metal fluorides. Optical films such as anti-reflective (AR) or high reflective coatings are of much interest and consist of alternating dielectric layers of low and high refractive index materials. Regarding the general procedure for the metal fluorides a novel nonaqueous sol-gel synthesis starting from metal alkoxides and alcohol-dissolved HF was used. The coatings were dried and calcined at 100 °C. The morphology of these films was characterised with REM, TEM and AFM. EDX and XPS were used to indentify the chemical composition and ellipsometry and UV-vis spectroscopy to determine the optical properties of the films. This new process allows the preparation of homogeneous magnesium fluoride and titanium dioxide layers with low roughness (Ra < 2.0 nm) on Si and SiO2 substrates. The thicknesses of the MgF2 and TiO2 single layers were adjustable between 25 nm and 500 nm depending on the number of coating steps and on the concentration of the used sols. The MgF2 layers had a refractive index of n500 = 1.36 and the TiO2 layers a refraction index of n500 = 2.05. For the first time, an alternating metal fluoride and oxide multilayer system was produced with a low temperature sol-gel method (consisting of MgF2 and TiO2). Based on the determined optical constants of the MgF2 and TiO2 single layers, AR and HR multilayer systems were calculated and fabricated. The transmission spectra of the designs and the corresponding multilayer were in good agreement. Similar results were obtained with the reflection spectra determined with spectral ellipsometry. The presented investigations were able to show that the developed low temperature sol-gel process using the spin-coating technique is suitable for the preparation of simple AR and HR multilayer systems.
Zugriffsstatistik: Die Daten für die Zugriffsstatistik der einzelnen Dokumente wurden aus den durch AWStats aggregierten Webserver-Logs erstellt. Sie beziehen sich auf den monatlichen Zugriff auf den Volltext sowie auf die Startseite. Die Zugriffsstatistik wird nicht standardisiert erfasst und kann maschinelle Zugriffe enthalten.
 
Bei Formatversionen eines Dokuments, die aus mehreren Dateien bestehen (insbesondere HTML), wird jeweils der monatlich höchste Zugriffswert auf eine der Dateien (Kapitel) des Dokuments angezeigt.
 
Um die detaillierten Zugriffszahlen zu sehen, fahren Sie bitte mit dem Mauszeiger über die einzelnen Balken des Diagramms.
Startseite: 4 Zugriffe PDF: 10 Zugriffe Startseite: 4 Zugriffe PDF: 4 Zugriffe Startseite: 10 Zugriffe PDF: 8 Zugriffe Startseite: 1 Zugriffe PDF: 8 Zugriffe Startseite: 5 Zugriffe PDF: 11 Zugriffe Startseite: 1 Zugriffe PDF: 6 Zugriffe Startseite: 5 Zugriffe PDF: 9 Zugriffe PDF: 33 Zugriffe PDF: 21 Zugriffe Startseite: 2 Zugriffe PDF: 9 Zugriffe Startseite: 5 Zugriffe PDF: 19 Zugriffe Startseite: 2 Zugriffe PDF: 13 Zugriffe PDF: 20 Zugriffe PDF: 29 Zugriffe PDF: 28 Zugriffe PDF: 34 Zugriffe Startseite: 2 Zugriffe PDF: 39 Zugriffe Startseite: 2 Zugriffe PDF: 43 Zugriffe Startseite: 1 Zugriffe PDF: 31 Zugriffe Startseite: 2 Zugriffe PDF: 17 Zugriffe Startseite: 3 Zugriffe PDF: 37 Zugriffe PDF: 39 Zugriffe Startseite: 4 Zugriffe PDF: 43 Zugriffe Startseite: 1 Zugriffe PDF: 39 Zugriffe PDF: 27 Zugriffe Startseite: 7 Zugriffe PDF: 30 Zugriffe Startseite: 4 Zugriffe PDF: 46 Zugriffe PDF: 44 Zugriffe Startseite: 2 Zugriffe PDF: 46 Zugriffe Startseite: 6 Zugriffe PDF: 51 Zugriffe Startseite: 1 Zugriffe PDF: 59 Zugriffe Startseite: 2 Zugriffe PDF: 45 Zugriffe Startseite: 3 Zugriffe PDF: 65 Zugriffe Startseite: 4 Zugriffe PDF: 47 Zugriffe Startseite: 4 Zugriffe PDF: 55 Zugriffe Startseite: 6 Zugriffe PDF: 32 Zugriffe Startseite: 11 Zugriffe PDF: 26 Zugriffe Startseite: 29 Zugriffe PDF: 49 Zugriffe Startseite: 30 Zugriffe PDF: 37 Zugriffe
Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
Apr
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Apr
14
May
14
Jun
14
Jul
14
Aug
14
Sep
14
Oct
14
Nov
14
Monat Jul
11
Aug
11
Sep
11
Oct
11
Nov
11
Dec
11
Feb
12
Apr
12
May
12
Jun
12
Jul
12
Aug
12
Sep
12
Oct
12
Nov
12
Dec
12
Jan
13
Feb
13
Mar
13
Apr
13
May
13
Jun
13
Jul
13
Aug
13
Sep
13
Oct
13
Nov
13
Dec
13
Jan
14
Feb
14
Mar
14
Apr
14
May
14
Jun
14
Jul
14
Aug
14
Sep
14
Oct
14
Nov
14
Startseite 4 4 10 1 5 1 5     2 5 2         2 2 1 2 3   4 1   7 4   2 6 1 2 3 4 4 6 11 29 30
PDF 10 4 8 8 11 6 9 33 21 9 19 13 20 29 28 34 39 43 31 17 37 39 43 39 27 30 46 44 46 51 59 45 65 47 55 32 26 49 37

Gesamtzahl der Zugriffe seit Jul 2011:

  • Startseite – 163 (4.18 pro Monat)
  • PDF – 1209 (31 pro Monat)
 
 
Generiert am 17.12.2014, 08:50:18