Logo of Humboldt-Universität zu BerlinLogo of Humboldt-Universität zu Berlin
edoc-Server
Open-Access-Publikationsserver der Humboldt-Universität
de|en
Header image: facade of Humboldt-Universität zu Berlin
View Item 
  • edoc-Server Home
  • Qualifikationsarbeiten
  • Dissertationen
  • View Item
  • edoc-Server Home
  • Qualifikationsarbeiten
  • Dissertationen
  • View Item
JavaScript is disabled for your browser. Some features of this site may not work without it.
All of edoc-ServerCommunity & CollectionTitleAuthorSubjectThis CollectionTitleAuthorSubject
PublishLoginRegisterHelp
StatisticsView Usage Statistics
All of edoc-ServerCommunity & CollectionTitleAuthorSubjectThis CollectionTitleAuthorSubject
PublishLoginRegisterHelp
StatisticsView Usage Statistics
View Item 
  • edoc-Server Home
  • Qualifikationsarbeiten
  • Dissertationen
  • View Item
  • edoc-Server Home
  • Qualifikationsarbeiten
  • Dissertationen
  • View Item
2015-12-17Dissertation DOI: 10.18452/17393
Adsorption on metal-supported silicate films
surface and sub-surface chemistry
Emmez, Emre
Mathematisch-Naturwissenschaftliche Fakultät
Die grundlegenden Aspekte chemischer Reaktionen auf Oberflächen können anhand von geeigneten Modelsystemen unter Vakuumbedingungen untersucht werden. Siliciumdioxid (SiO2) als wichtiges Material für hochmoderne Technologieanwendungen in der Mikroelektronik, Photonik und Katalyse, war Gegenstand zahlreicher Studien, um die Beziehungen zwischen der atomaren Struktur und funktionalen Eigenschaften von Silizium-basierten Materialien zu erklären. Diese Arbeit untersucht die Wechselwirkung von Gasen mit epitaktisch gewachsenen Silikat-Dünnschichten auf einem Ru(0001) Einkristall. Unter Verwendung von Infrarot-Reflexions-Absorptions-Spektroskopie (IRAS) und temperaturprogrammierter Desorptionspektroskopie (TPD) konnten die Hydroxy-Spezies auf reinen Silikatfilmen als isolierte Silanole (Si-OH) identifiziert werden. Isotopenexperimente haben gezeigt, dass sich thermisch stabile Oberflächenhydroxylate hauptsächlich aus der Adsorption von Wassermolekülen bilden. Ein Austausch der Silanole mit Sauerstoffatomen im Kristallgitter während des Dehydroxylierungsprozesses wurde nicht beobachtet. Durch die Adsorption von Gasen wie CO, H2 und O2 bei erhöhtem Druck, lässt sich auf komplexere Prozesse schließen. Dies beinhaltet Gastransport durch Poren im Film, was mit strukturellen Defekten in dem Silikatfilm verbunden ist, sowie nachfolgende Adsorption und Diffusion auf dem unterliegenden Ru(0001)-Substrat. Während der Einlagerung der Moleküle in die Silikatschicht bleibt der Oxidfilm auch unter hohem Druck (~ 10 mbar) sowie hoher Temperatur (~900 K) intakt. Solch ein Hybridsystem, welches eine robuste Siliciumdioxidmembran mit einem sich darunter befindlichen, chemisch aktiven Metall kombiniert, könnte ein interessantes Materialsystem für technische Anwendungen darstellen, insbesondere zur Herstellung von Katalysatoren und Sensoren sowie für Korrosionsanwendungen.
 
The fundamental aspects of the chemical reactions at surfaces can be elucidated by using well-defined model systems under the controlled conditions provided by vacuum-based techniques. Silicon dioxide (SiO2) as one of the crucial materials in modern technological applications, including microelectronics, photonics, and catalysis, has been subjected to numerous studies in order to rationalize relationships between the atomic structure and functional properties of silica-based materials. This work marks the attempt to understand interaction of ambient gases with a well-ordered, ultrathin silicate film grown on a Ru(0001) substrate. Using infrared reflection absorption spectroscopy (IRAS) and temperature programmed desorption (TPD), hydroxo species, primarily in the form of isolated silanols (Si-OH), were identified on pristine silicate films. Isotopic experiments demonstrated that surface hydroxyls form primarily from the water molecules. Silanols do not undergo scrambling with the lattice oxygen atoms upon dehydroxylation. Steps on a silicate sheet and/or “holes” in these ultrathin films are proposed as active sites for hydroxylation. Adsorption of gases such as CO, H2 and O2 at elevated pressures revealed a more complex behavior. It involves gas transport through the pores, associated with structural defects in the silicate film, subsequent adsorption, and diffusion across the Ru(0001) surface underneath. During this intercalation, the silicate film stays intact even under high pressure (~10 mbar) and high temperature conditions (~900 K). The silicate layer does however strongly passivate the Ru surface towards RuO2(110) formation that readily occurs on bare Ru(0001) under the same conditions. Such a hybrid system, which combines a robust silica “membrane” and a chemically active metal underneath, could become an interesting material for technological applications, in particular in catalysis, sensors and anti-corrosion applications.
 
Files in this item
Thumbnail
emmez.pdf — Adobe PDF — 21.67 Mb
MD5: df2daa35638da1dfec3daa4f10571b3b
Cite
BibTeX
EndNote
RIS
Namensnennung - Keine kommerzielle Nutzung - Keine BearbeitungNamensnennung - Keine kommerzielle Nutzung - Keine BearbeitungNamensnennung - Keine kommerzielle Nutzung - Keine BearbeitungNamensnennung - Keine kommerzielle Nutzung - Keine Bearbeitung
Details
DINI-Zertifikat 2019OpenAIRE validatedORCID Consortium
Imprint Policy Contact Data Privacy Statement
A service of University Library and Computer and Media Service
© Humboldt-Universität zu Berlin
 
DOI
10.18452/17393
Permanent URL
https://doi.org/10.18452/17393
HTML
<a href="https://doi.org/10.18452/17393">https://doi.org/10.18452/17393</a>