2017-07-11Dissertation DOI: 10.18452/18036
Growth Kinetics, Thermodynamics, and Phase Formation of group-III and IV oxides during Molecular Beam Epitaxy
dc.contributor.authorVogt, Patrick
dc.date.accessioned2017-07-11T13:38:27Z
dc.date.available2017-07-11T13:38:27Z
dc.date.issued2017-07-11
dc.identifier.urihttp://edoc.hu-berlin.de/18452/18700
dc.description.abstractDie vorliegende Arbeit präsentiert eine erste umfassende Wachstumsstudie, und erste quantitative Wachstumsmodelle, von Gruppe-III und IV Oxiden synthetisiert mit sauerstoffplasmaunterstützter Molekularstrahlepitaxie (MBE). Diese entwickelten Modelle beinhalten kinetische und thermodynamische Effekte. Die erworbenen Erkenntnisse sind auf fundamentale Wachstumsprozesse in anderen Syntheseverfahren übertragbar, wie zum Beispiel der Laserdeposition oder metallorganische Gasphasenepitaxie. Die Wachstumsraten und Desorptionsraten werden in-situ mit Laser-Reflektometrie bzw. Quadrupol-Massenspektrometrie (QMS) bestimmt. Es werden die transparenten halbleitenden Oxide Ga2O3, In2O3 und SnO2 untersucht. Es ist bekannt, dass sich das Wachstum von Gruppe-III und IV Oxiden, aufgrund der Existenz von Suboxiden, fundamental von anderen halbleitenden Materialien unterscheidet. Es stellt sich heraus, dass die Wachstumsrate der untersuchten binären Oxide durch die Formierung und Desorption von Suboxiden flussstöchiometrisch und thermisch limitiert ist. Es werden die Suboxide Ga2O für Ga2O3, In2O für In2O3 und SnO für SnO2 identifiziert. Ein Suboxid ist ein untergeordneter Oxidationszustand, und es wird gezeigt, dass die untersuchten Oxide über einen Zwei-Stufen-Prozess gebildet werden: vom Metall zum Suboxid, und weiterer Oxidation vom Suboxid zum thermodynamisch stabilen festen Metalloxid. Dieser Zwei-Stufen-Prozess ist die Basis für die Entwicklung eines ersten quantitativen, semiempirschen MBE-Wachstumsmodells für binare Oxide die Suboxide besitzen. Dieses Model beschreibt und erklärt die gemessenen Wachstumsraten und Desorptionsraten. Es wird die Kinetik und Thermodynamik des ternären Oxidsystems (InxGa1−x)2O3 untersucht. Die gemittelten Einbauraten von In und Ga in ein makroskopisches Volumen von (InxGa1−x)2O3 Dünnschichten werden ex-situ mit energiedispersiver Röntgenspektroskopie gemessen. Diese Einbauraten werden systematisch analysiert und im Rahmen kinetischer und thermodynamischer Grenzen beschrieben. Es wird gezeigt, dass Ga den In-Einbau in (InxGa1−x)2O3 aufgrund seiner stabileren Ga–O Bindungen thermodynamisch verhindert. In diesen Zusammenhang wird ein neuer katalytisch-tensidischer Effekt des In auf den Einbau von Ga gefunden. Eine Folge dieses katalytisch-tensidischen Effektes ist die Formierung der thermodynamisch, metastabilen hexagonalen Ga2O3 phase mit sehr hoher Kristallqualität. Ein thermodynamisch induziertes, kinetisches Wachstumsmodel für (InxGa1−x)2O3 wird entwickelt, mit dem sich alle makroskopischen Metall-Einbauraten und Desorptionsraten vorhersagen lassen. Mögliche (InxGa1−x)2O3 Strukturen gewachsen mit MBE werden mittels Röntgenkristallographie bestimmt. Mit Hilfe der Röntgenstrukturanalyse wird ein erster makroskopischer Ansatz zur Bestimmung der mikroskopischen In Konzentration X in möglichen (InXGa1−X)2O3 Phasen hergeleitet. Es werden Löslichkeitsgrenzen von In bzw. Ga in monoklinem und kubischem (InXGa1−X)2O3 bestimmt.ger
dc.description.abstractThe present thesis presents a first comprehensive growth investigation and first quantitative growth models of group-III and IV oxides synthesized by oxygen plasma-assisted molecular beam epitaxy (MBE). The developed models include kinetic and thermodynamic effects. The obtained findings are generally valid for fundamental growth processes in other growth techniques, such as pulsed laser deposition and metal-organic vapor phase-epitaxy. The growth rates and desorption rates are measured in-situ by laser reflectometry and quadrupole mass spectrometry (QMS), respectively. The binary transparent semiconducting oxides Ga2O3, In2O3, and SnO2 are investigated. It is known that the growth of group-III and IV oxides is fundamentally different as compared to other semiconductor compounds and due to the existence of suboxides. It is found that the growth rate of the binary oxides investigated is flux-stoichiometrically and thermally limited by the formation and desorption of their respective suboxide. These suboxides are identified as Ga2O for Ga2O3, In2O for In2O3, and SnO for SnO2. A suboxide is a lower oxidation state, and it is shown, that the investigated oxides grow via a two-step oxidation process. That means, all metal oxidizes to the suboxide, and the suboxide can be further oxidized to the thermodynamic stable solid metal-oxide. This two-step oxidation process is the basis for the development of a first quantitative semi-empirical MBE growth model which predicts and explains the measured growth rates and desorption rates, for binary oxides possessing suboxides. The kinetics and thermodynamics of the ternary oxide system (InxGa1−x)2O3, grown by MBE, is investigated. The average In and Ga incorporation rates into a macroscopic volume of (InxGa1−x)2O3 are measured ex-situ by energy dispersive X-ray spectroscopy. These incorporation rates are systematically analyzed and explained in the framework of kinetic and thermodynamic limitations. It is shown that Ga thermodynamically inhibits the incorporation of In into (InxGa1−x)2O3 due to its stronger Ga–O bonds. In this context, a new catalytic-surfactant effect of In on the formation of Ga2O3 is found. As a consequence of this catalytic-surfactant effect the metastable hexagonal Ga2O3 with very high crystal quality is formed. A thermodynamically induced kinetic growth model for (InxGa1−x)2O3 MBE is developed. It predicts all macroscopic metal incorporation rates and desorption rates. Possible (InxGa1−x)2O3 phases grown by MBE are investigated by X-ray crystallography. By means of X-ray diffraction analysis, a first macroscopic approach to determine the microscopic In concentration X in possible (InXGa1−X)2O3 phases is derived. The solubility limits of In and Ga in monoclinic and cubic (InXGa1−X)2O3 phases, respectively, are identified.eng
dc.language.isoeng
dc.publisherHumboldt-Universität zu Berlin
dc.rightsCC0 1.0 Universell
dc.rights.urihttp://creativecommons.org/publicdomain/zero/1.0/*
dc.subjectTransparente halbleitende Oxideger
dc.subjectSuboxideger
dc.subjectWachstumskinetikger
dc.subjectThermodynamikger
dc.subjectModellelierungger
dc.subjectKatalysatorger
dc.subjectTensidger
dc.subjectMolekularstrahlepitaxieger
dc.subjectTransparent semiconducting oxideseng
dc.subjectsuboxideseng
dc.subjectgrowth kineticseng
dc.subjectthermodynamicseng
dc.subjectmodelingeng
dc.subjectcatalysteng
dc.subjectsurfactant, molecular beam epitaxyeng
dc.subject.ddc530 Physik
dc.titleGrowth Kinetics, Thermodynamics, and Phase Formation of group-III and IV oxides during Molecular Beam Epitaxy
dc.typedoctoralThesis
dc.identifier.urnurn:nbn:de:kobv:11-110-18452/18700-8
dc.identifier.doihttp://dx.doi.org/10.18452/18036
dc.date.accepted2017-06-09
dc.contributor.refereeRiechert, Henning
dc.contributor.refereeMasselink, W. Ted
dc.contributor.refereeSpeck, James S.
dc.subject.rvkUP 7550
local.edoc.pages135
local.edoc.type-nameDissertation